Download X Jampilen RP120L Product Data And Technical Information Description "Jampilen RP120L" is a low sealing temperature polypropylene resin. The product is designed for BOPP films and is formulated with standard processing stabilization and is calcium stearate free. "Jampilen RP120L" exhibits very high transparency, excellent gloss and outstanding heat weldability. Films from "Jampilen RP120L" show good hot tack and low seal initiation temperature (115 to 120 0C). "Jampilen RP120L" is suitable for the production of shrinkable coextruded BOPP film for display packaging of cheese, bakery and meet products. "Jampilen RP120L" is suitable for food contact. Product processing method Extrusion Feature Terpolymer, Very high transparency, Good heat weldability, High resistance to oxygen, moisture, fats and oils, Excellent transparency and gloss Appplication Sealing layers of oriented and non-oriented films, Packaging for food, cosmetics, clothes and cigarettes, Shrinkable coextruded BOPP film for display packaging of cheese, bakery and meat products, Breathable film, lamination film, stationery film Product polymer type Terpolymer Product grade name RP120L Product packing type 6.0 kg packaging Property Value Unit Test Method Property Melt Flow Rate (230 0C, 2.16 kg) Value 6 Unit gr/10min Test Method ASTM D1238 Property Density Value 0.9 Unit g/cm³ Test Method ASTM D1505 Property Flexural Modulus Value 700 Unit MPa Test Method ASTM D790 Property Tensile Strength at Yield Value 22 Unit MPa Test Method ASTM D638 Property Tensile Elongation at Yield Value 12 Unit % Test Method ASTM D638 Property Izod Impact Strength (notched) at 23 0C Value 80 Unit J/m Test Method ASTM D638 Property Vicat softening point (B 1200C/h,10N) Value 115 Unit °C Test Method ASTM D1525 Property H.D.T (0.45 Mpa) Value 60 Unit °C Test Method ASTM D648 Property Accelerated oven ageing in air at 150 0C Value 360 Unit hours Test Method ASTM D3012 Property Haze (20 μm) Value 1 Unit % Test Method ASTM D1003 Property Gloss (450) Value 85 Unit ---- Test Method ASTM D2543